PP Homopolymer for Extrusion
This high‑performance homopolymer polypropylene fiber‑grade resin is engineered for fiber extrusion and spinning processes. Featuring a melt‑flow rate of 3.2, L5E89 delivers balanced tensile strength, excellent spinnability and stable continuous‑processing adaptability. It is well‑suited for fiber‑based end‑products with stringent tensile‑property requirements, such as woven sacks, geotextile fibers, ropes and non‑woven fabrics.
Typical property values for guidance. Certified lot-specific COA provided with every shipment.
| Property | Test Method | Unit | Typical Value |
|---|---|---|---|
| Melt Flow Rate | ASTM D1238 | g/10min | 3.0-3.4 |
| Density | ASTM D1505 | g/cm³ | 0.905 |
| Tensile Strength (Yield) | ASTM D638 | MPa | 35 |
| Elongation at Break | ASTM D638 | % | 200 |
| Flexural Modulus | ASTM D790 | MPa | 1500 |
| Notched Izod Impact (23°C) | ASTM D256 | kJ/m² | 3.5 |
| Rockwell Hardness | ASTM D785 | R scale | 100 |
| Vicat Softening Temperature | ASTM D1525 | °C | 155 |
| Heat Deflection Temperature (0.45 MPa) | ASTM D648 | °C | 110 |
Test condition: 230°C / 2.16 kg for MFR. Values are typical and not intended as specification limits.
Typical end-use applications for L5E89 — confirmed by mill technical data and converter feedback.
industrial woven sacks, grain packaging sacks, fertilizer sacks, FIBC base fabric
PP baling ropes, split‑film ropes, engineering ropes, decorative fiber filaments
geotextile fibers, non‑woven fabric raw material, protective textile base material
fiber‑grade homopolymer PP base resin for fiber‑oriented compounding and pelletizing
L5E89 processes on standard equipment. Use the guideline below as a starting point; fine-tune to your specific mold and cycle.
| Extrusion Temperature | 190 – 230 °C |
| Die Temperature | 210 – 230 °C |
| Draw Ratio | 1:6 – 1:9 |
| Quench Water Temperature | 20 – 40 °C |
| Annealing Temperature | 120 – 140 °C |
Standard mill packaging protects resin integrity through ocean and inland transit to your destination port.
25kg Bag
1,000 kg bulk bag for high-volume converters seeking reduced packaging waste.
Each shipment includes mill COA, MSDS, packing list, and certificate of origin. Third-party SGS/BV inspection available on request.
Tell us your volume, destination port, and packaging preference. We'll respond within 24 hours with mill-direct pricing and current availability from our mill partners.